Titanium
Grade 5
TA6V
Ti6Al4V grade 5 is an alpha-beta titanium alloyed with aluminium and vanadium. It offers an excellent compromise between mechanical resistance, toughness and ductility. Furthermore, its machinability makes it easy to weld.
Key benefits
Corrosion resistance
Formability
Weldability
Normes
ASTM F1472
AMS 4935
ISO 5832-3
Available forms in stock
Diameter
- 8 mm to 100 mm
Length
- 3000 mm approx.
Dimensions
- Any kind of granulometry suitable to your machine
Diameter
- 3 to 50.8 mm
Thickness
- 0.3 to 5 mm
Diameter
- 3 to 50.8 mm
Thickness
- 0.3 to 5 mm
Normes
ASTM B348
ASTM B265
Available forms in stock
Diameter
- 10 mm to 260 mm
Length
- 3000 mm approx.
Thickness
- 5 mm to 60 mm
Width
- 1000 to 2000 mm
Length
- 1000 to 6000 mm
Hexagonal head screw
- DIN 931/933
Hexagonal hollowed cylindric screw
- DIN 912
Hexagonal hollowed milled head screw
- DIN 7991
Cylindric split head screw
- DIN 84
Cylindric split crowned head screw
- DIN 85
Split milled head screw
- DIN 963
Split crowned head screw
- DIN 964
Headless hexagonal hollowed screw
- DIN 916
Threated rod
- Standard length : 1 meter
- DIN 975
Hexagonal nuts/Brake/Collar
- DIN 934
- DIN 985 (brake)
Washer
- DIN 125
- DIN 127 (brake)
Stud
- DIN 938
Diameter
- 3 to 50.8 mm
Thickness
- 0.3 to 5 mm
Diameter
- 3 to 50.8 mm
Thickness
- 0.3 to 5 mm
Available forms in stock
Thickness
- From 100mm
Width
- On demand
Normes
AMS 4911
AMS 4928
ASTM B265
ABS 5326C
AIMS 03-18-006
ASNA 3200
ABS 5125A
AIMS 03-18-001
ASNA 3304
WL 3.7164.1
LN 9297
ABS 5453A
ASNA 3307
ABS 5125B
ABS 5125C
Available forms in stock
Diameter
- 6 mm to 320 mm
Length
- 2000 to 4000 mm around
Thickness
- 0,4 mm to 110 mm
Width
- 1000 to 2000 mm
Length
- 1000 to 6000 mm
Diameter
- 3 to 50.8 mm
Thickness
- 0.3 to 5 mm
Diameter
- 3 to 50.8 mm
Thickness
- 0.3 to 5 mm
Available forms in stock
Thickness
- According to plans
Width
- According to plans
Chemical composition
Reference standard : ASTM B348
Fe
- 0% min
- 0,4% max
O
- 0% min
- 0,2% max
N
- 0% min
- 0,05% max
C
- 0% min
- 0,08% max
H
- 0% min
- 0,015% max
Al
- 5,5% min
- 6,75% max
V
- 3,5% min
- 4,5% max
Ti
- —
- Balance
Back
Mechanical properties
Rm (Mpa)
895
Rp 0,2 (MPA)
828
Density (g/cm3)
4,43
A (%)
10