Titanium
Grade 9
Ti3Al-2.5V
Grade 9 titanium offers a better weldability, mechanical resistance and formability than TA6V. This metal is mainly used in aerospace but also for bicycle frames and golf clubs.
Key benefits
Weldability
Normes
ISO 15156
NACE MR0175
ASTM B265
ASTM B337
ASTM B338
ASTM B348
ASTM B381
ASTM B861
ASTM B862
Available forms in stock
Diameter
- 0.4 mm to 300 mm
Length
- 3000 mm approx.
Thickness
- 0,4 mm to 60 mm
Width
- 1000 to 2000 mm
Length
- 1000 to 6000 mm
Diameter
- 2 mm to 10 mm
Diameter
- from 3 to 50,8 mm
Thickness
- from 0,3 to 5 mm
Diameter
- from 3 to 50,8 mm
Thickness
- from 0,3 to 5 mm
Normes
AMS 4943
AMS 4944
Available forms in stock
Diameter
- 0.4 mm to 300 mm
Length
- 3000 mm approx.
Thickness
- 0,4 mm to 60 mm
Width
- 1000 to 2000 mm
Length
- 1000 to 6000 mm
Diameter
- 0,32 mm to 10 mm
Diameter
- from 3 to 50,8 mm
Thickness
- from 0,3 to 5 mm
Diameter
- from 3 to 50,8 mm
Thickness
- from 0,3 to 5 mm
Chemical composition
O
- 0% min
- 0,15% max
N
- 0% min
- 0,03% max
C
- 0% min
- 0,08% max
H
- 0% min
- 0,015% max
Fe
- 0% min
- 0,25% max
Al
- 2,5% min
- 3,5% max
V
- 2,0% min
- 3,0% max
Ti
- —
- Balance
Back
Mechanical properties
Rm (Mpa)
620
Rp 0,2 (Mpa)
483
Density (g/cm3)
4,48
A (%)
15
Z %
25