Titanium
Ti-6Al-2Sn-4Zr-6Mo
Ti6-2-4-6 is a heat treated alpha-beta titanium alloy for which you can get higher properties than TA6V. Its strengths are a better resistance, a low cycle fatigue and a good ductility. It can resist to tempratures up to 450°C. This metal is mainly used for turbines, discs or blades.
Key benefits
Low elasticity modulus
Low density/weight ratio
Fatigue resistance
Normes
MIL F - 83142A Comp 11 Frg Amin
MIL F - 8314 Comp 11 Frg Ht
MIL T - 9047G
Available forms in stock
Diameter
- 12 mm to 150 mm
Length
- 3000 mm approx.
Thickness
- 1,6 mm to 40 mm
Normes
AMS 4981B
Available forms in stock
Diameter
- 12 mm to 150 mm
Length
- 3000 mm approx.
Thickness
- 1,6 mm to 40 mm
Chemical composition
Reference standard : AMS 4981
Al
- 5,5% min
- 6,5% max
C
- 0% min
- 0,04% max
Sn
- 1,75% min
- 2,25% max
N
- 0% min
- 0,04% max
Zr
- 3,5% min
- 4,5% max
H
- 0% min
- 0,0125% max
Mo
- 5,5% min
- 6,5% max
Cu
- 0% min
- 0,5% max
Fe
- 0% min
- 0,15% max
O
- 0% min
- 0,15% max
Ti
- —
- Balance
Back
Mechanical properties
Rm (Mpa)
1034
Rp 0,2 (Mpa)
965
Density (g/cm3)
4,64
A (%)
6
Z%
15