Nickel Alloys
K-500
2.4375
K500 is a quench hardenable nickel-tin alloy. Thanks to titanium and aluminium addition, it gets a good corrosion resistance to seawater, hydrofluoric acid, sulfuric acid and alkaline.
Key benefits
Corrosion resistance
Low permeability
Age hardenable
Normes
ASTM B865
AMS 4676
Available forms in stock
Diameter
- from 5 to 300 mm
Thicknesses
- from 0,4 to 50 mm
Dimensions
- 1000*2000 mm
Granulometry
- from 15 microns to 60 microns
Diameter
- from 10 mm to 50,8 mm
Thickness
- from 1 mm to 5 mm
Normes
ASTM B865
AMS 4676
Available forms in stock
Diameter
- from 5 to 301 mm
Thicknesses
- from 0,4 mm to 50 mm
Dimensions
- 1000*2000 mm
Granulometry
- from 15 microns to 60 microns
Diameter
- from 10 mm to 50,8 mm
Thickness
- from 1 mm to 5 mm
Normes
ASTM B865
AMS 4676
Available forms in stock
Diameter
- from 5 to 300 mm
Thicknesses
- from 0,4 to 50 mm
Dimensions
- 1000*2000 mm
Granulometry
- from 15 microns to 60 microns
Diameter
- from 10 mm to 50,8 mm
Thickness
- from 1 mm to 5 mm
Chemical composition
C
- 0% min
- 0,25% max
Mn
- 0% min
- 1,5% max
Si
- 0% min
- 0,5% max
S
- 0% min
- 0,01% max
Ni
- 63% min
- 70% max
Cu
- 27% min
- 33% max
Ti
- 0,35% min
- 0,85% max
Al
- 2,3% min
- 3,15% max
Fe
- 0
- 2
Back
Mechanical properties
RM (MPA)
1100
RP 0,2 (MPA)
690
Density (G/CM3)
8.44
A (%)
24%