Nickel Alloys
A-286
1.4980
A-286 alloy is an age-hardened tin base super alloy. Well used for applications which require a high resistance to temperatures from -195°C to 538°C. Resistance to oxidisation is high to allow continuous operation at 816°C.
Key benefits
Very strong and good corrosion resistance at high temperatures
Age-hardenable
Normes
AMS 5731
AMS 5732
AMS 5734
AMS 5525
ASTM A453
ASTM A638
Available forms in stock
Diameter
- from 5 to 300 mm
Thicknesses
- from 0,4 to 50 mm
Dimensions
- 1000*2000 mm
Granulometry
- from 15 microns to 60 microns
Diameter
- from 10 mm to 50,8 mm
Thickness
- from 1 mm to 5 mm
Normes
AMS 5731
AMS 5732
AMS 5734
AMS 5525
ASTM A453
ASTM A638
Available forms in stock
Diameter
- from 5 to 300 mm
Thicknesses
- from 0,4 mm to 50 mm
Dimensions
- 1000*2000 mm
Granulometry
- from 15 microns to 60 microns
Diameter
- from 10 mm to 50,8 mm
Thickness
- from 1 mm to 5 mm
Normes
AMS 5731
AMS 5732
AMS 5734
AMS 5525
ASTM A453
ASTM A638
Available forms in stock
Diameter
- from 5 to 300 mm
Thicknesses
- from 0,4 to 50 mm
Dimensions
- 1000*2000 mm
Granulometry
- from 15 microns to 60 microns
Diameter
- from 10 mm to 50,8 mm
Thickness
- from 1 mm to 5 mm
Chemical composition
Cr
- 13,5% min
- 16,5% max
NI
- 24,5% min
- 27,5% max
MO
- 1,5% min
- 1,55% max
CO
- 0% min
- 1,5% max
VA
- 0,15% min
- 0,55% max
AL
- 0% min
- 0,35% max
TI
- 1,9% min
- 2,35% max
B
- 0,003% min
- 0,01% max
C
- 0% min
- 0,08% max
MN
- 0% min
- 2,5% max
SI
- 0% min
- 1,5% max
P
- 0% min
- 0,025% max
S
- 0% min
- 0,025% max
Fe
- —
- Balance
Back
Mechanical properties
Rm (Mpa)
999,7 (21°)
Rp 0,2 (Mpa)
655,5 (21°)
Density (g/cm3)
7,93
A (%)
24,5 (21°)