Stainless steel
316 L (ESR/VAR)
1.4441
Cold worked
316L (1.4441) is an austenitic stainless steel whose basic composition is similar to the 316L (1.4435), except with a much stricter tolerance to impurities. This gives the steel a better resistance to corrosion than ordinary 316L, making it more suitable for medical applications (and especially implants).
Avantages
Excellent corrosion resistance
Biocompatibility
For implants and instruments
Normes
ASTM F138
ASTM F139
ISO 5832-1
Formes disponibles en stock
Diameter
- 5 to 19 mm
Length
- 3000 mm approx.
Granulometry
- Any kind of granulometry suitable to your machine
Formes disponibles sur demande
Thickness
- 1 mm to 6 mm
Dimensions
- 300 mm to 320 mm (foils)
- 1000 mm (sheets and plates)
Diameter
- 3 to 50.8 mm
Thickness
- 0.3 to 5 mm
Diameter
- 3 to 50.8 mm
Thickness
- 0.3 to 5 mm
Composition chimique
Reference standard : ASTM F138
C
- 0% min
- 0,03% max
Si
- 0% min
- 0,75% max
Mn
- 0% min
- 2% max
P
- 0% min
- 0,025% max
S
- 0% min
- 0,01% max
Cr
- 17% min
- 19% max
Mo
- 2,25% min
- 3% max
Ni
- 13% min
- 15% max
Cu
- 0% min
- 0,5% max
N
- 0% min
- 0,1% max
Fe
- —
- Balance
Haut de page
Caractéristiques mécaniques
Rm (Mpa)
860 ≤ Rm ≤ 1100
Rp 0,2 (Mpa)
690
Density (g/cm3)
7.9
A (%)
12